Low-alloy high-strength steel Q460 thick plates were welded by CO2 gas shielded arc welding with solid wire and flux-cored wire at different heat inputs (12.6, 16.4, 19.5 kJ·cm-1). The effects of welding wire and heat input on the microstructure and tensile properties of the joint were investigated. The results show that the proportion of acicular ferrite in columnar grain zone in weld zone of the two joints decreased and the grain boundary ferrite of large size increased with the increase of heat input. The hardness of weld zone of the joint welded with solid wire changed little with the increase of heat input,but that of the joint welded with flux-cored wire decreased significantly. The yield strength and ultimate tensile strength of the joint welded with solid wire were similar to those of base metal whereas the elongation was lower than that of base metal; the elongation decreased with the increase of heat input. The strenth of the joint welded with flux-cored wire was equivalent to that of the base metal at lower heat input. The increase of heat input obviously reduced the tensile strength, but affected the yield strength and elongation slightly.
引用该论文:FENG Xiangli,WANG Lei,LIU Yang. Effect of Welding Material and Heat Input on Tensile Property of Welded Joint of Q460 Steel Thick Plate[J]. Materials for mechancial engineering, 2019, 43(3): 1～6 冯祥利,王磊,刘杨. 焊接材料及热输入对Q460钢厚板焊接接头拉伸性能的影响[J]. 机械工程材料, 2019, 43(3): 1～6
【1】WANG W, LIU T, LIU J. Experimental study on post-fire mechanical properties of high strength Q460 steel[J]. Journal of Constructional Steel Research, 2015, 114:100-109.
【2】WANG L, BASU P K, LEIVA J P. Automobile body reinforcement by finite element optimization[J]. Finite Elements in Analysis and Design, 2004, 40(8):879-893.
【3】KANG J, WANG C, WANG G D. Microstructural characteristics and impact fracture behavior of a high-strength low-alloy steel treated by intercritical heat treatment[J]. Materials Science and Engineering:A, 2012, 553:96-104.
【4】HAN G, XIE Z J, XIONG L, et al. Evolution of nano-size precipitation and mechanical properties in a high strength-ductility low alloy steel through intercritical treatment[J]. Materials Science and Engineering:A, 2017, 705:89-97.
【5】CAO X J, WANJARA P, BERNARD A, et al. Hybrid fiber laser-arc welding of high strength low alloy steel[J]. Materials Science Forum, 2014, 783:663-668.
【6】NATHAN S R, BALASUBRAMANIAN V, MALARVIZHI S, et al. Effect of welding processes on mechanical and microstructural characteristics of high strength low alloy naval grade steel joints[J].Defence Technology,2015,11(3):308-317.
【10】MA T Y, HU Y F, LIU X, et al. Experimental investigation into high strength Q690 steel welded H-sections under combined compression and bending[J]. Journal of Constructional Steel Research, 2017, 138:449-462.
【15】TSUYAMA T, NAKAI K, AKIYAMA M, et al. Effects of microstructure on mechanical property in weld metal formed with the hot-wire method applying ordinal CO2 gas shielded arc welding method[J]. Journal of the Iron & Steel Institute of Japan, 2013, 99(7):468-474.
【16】WAHBA M, MIZUTANI M, KATAYAMA S. Hybrid welding with fiber laser and CO2 gas shielded arc[J]. Journal of Materials Processing Technology, 2015, 221:146-153.
【19】MA T Y, HU Y F, LIU X, et al. Experimental investigation into high strength Q690 steel welded H-sections under combined compression and bending[J]. Journal of Constructional Steel Research, 2017, 138:449-462.
【20】CHEN Z, XIONG Y, QIU H, et al. Stress intensity factor-based prediction of solidification crack growth during welding of high strength steel[J]. Journal of Materials Processing Technology, 2018, 252:270-278.
【21】LI X, SHANG C, MA X. Elemental distribution in the martensite-austenite constituent in intercritically reheated coarse-grained heat-affected zone of a high-strength pipeline steel[J]. Scripta Materialia, 2017, 139:67-70.